Styrolution Luran® S KR2866C ASA / PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Luran® S KR2866C ASA / PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Luran S KR2866C is a blend of ASA and PC with a reduced content of PC. It is characterized by a medium impact toughness and heat resistance.Good heat resistanceMedium impact strengthInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.90 % @Temperature 23.0 °C |
0.90 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ISO 294-4 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 110 MPa | 16000 psi | ISO 2039-1 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Elongation at Yield | 3.4 % | 3.4 % | ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 - 100 µm/m-°C | 44.4 - 55.6 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ISO 75 |
| Vicat Softening Point | 110 °C @Load 5.10 kg |
230 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Drying Temperature | 100 °C @Time 7200 - 14400 sec |
212 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Vistaflex® 671N Thermoplastic Rubber (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7777 PEEK, lubricant modified
- LG Chemical LUPOY GN5001RF PC/ABS, Halogen Free Flame Retardant
- SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer
- A. Schulman POLYBATCH™ Light Grey 80426U Concentrate Based In LLDPE
- Eagle Brass 220 Commercial Bronze, Hard
- Arkema Group Orgalloy® LE 60THM Flexible Nylon Alloy (Conditioned)
- 3M Scotchkote™ 80EG 531 Urethane Elastomer
- DSM Akulon® K240-HP Impact Modified Nylon 6 (European Grade) (Cond)
- Fainplast Compounds MPH 81 Medical Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved