Stellarchem MP-860Q TPE Compound
| Category | Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE |
| Manufacturer | Stellarchem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stellarchem MP-860Q TPE Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This grade of Stellarchem TPE is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, elastomeric polyolefin based, completely recyclable, colorable & non-hygroscopic thermoplastics elastomer material.Information provided by Stellarchem Polymer & Industrial
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
| Melt Flow | 7.86 g/10 min | 7.86 g/10 min | JIS K7210 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | JIS K6301 |
| Tensile Strength, Ultimate | 2.94 MPa | 427 psi | JIS K6301 |
| Elongation at Break | 617 % | 617 % | JIS K6301 |
| 100% Modulus | 0.01078 GPa | 1.564 ksi | JIS K6301 |
| 300% Modulus | 0.000686 GPa | 0.0996 ksi | JIS K6301 |
| Tear Strength | 21.8 kN/m | 124 pli | JIS K6301-B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 - 220 °C | 392 - 428 °F | Metering Temperature, Extrusion |
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| 160 - 180 °C | 320 - 356 °F | Extrusion | |
| Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| 180 - 200 °C | 356 - 392 °F | Transition, Extrusion | |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| 220 - 230 °C | 428 - 446 °F | Extrusion | |
| Nozzle Temperature | 220 - 230 °C | 428 - 446 °F | Injection Molding |
| Die Temperature | 195 - 210 °C | 383 - 410 °F | Extrusion |
| Melt Temperature | 150 - 230 °C | 302 - 446 °F | Injection Molding |
| 150 - 230 °C | 302 - 446 °F | Extrusion | |
| Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
| Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
| 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 H-GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced
- Saint-Gobain Rulon® 945 Grade Bearing/Seal PTFE
- Unifrax Fiberfrax® Washed 657 High Purity High-Index Fiber
- Unipetrol P III Propane
- Unipetrol SH Sorbent Chezacarb
- A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
- Clariant Renol 6622-L Nylon 66, Glass Fiber Filled, Lubricated
Copyright © lookpolymers.com All Rights Reserved