Spartech Royalite R632M Carbon Black Filled ABS/PVC Resin
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/PVC Alloy , Vinyl (PVC) |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech Royalite R632M Carbon Black Filled ABS/PVC Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer. This static-conductive material is UL®-listed and meets minimum static-decay requirements outlined in MIL-B-1705B and NFPA Code 56A specifications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hrs. ASTM D570 |
| Viscosity | 212400 cP @Shear Rate 3000 1/s, Temperature 191 °C |
212400 cP @Shear Rate 3000 1/s, Temperature 375 °F |
Melt Viscosity |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 0.21 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.21 g/10 min @Load 11.0 lb, Temperature 392 °F |
Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 72 | 72 | ASTM D785 |
| Tensile Strength, Yield | 31.3 MPa | 4540 psi | ASTM D638 |
| Modulus of Elasticity | 1.90 GPa | 276 ksi | ASTM D638 |
| Flexural Yield Strength | 48.4 MPa | 7020 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.400 J/cm @Temperature -20.0 °C |
0.749 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 166 µm/m-°C @Temperature 20.0 °C |
92.2 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 80.0 °C | 176 °F | ASTM D1525 |
| Flammability, UL94 | 5VA | 5VA | V-0/0.090 in. UL 94 |
| Oxygen Index | 30.4 % | 30.4 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1e+05 | 1e+05 | ASTM D257 |
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREWHITE PE 10-50
- Noble Polymers Ecobarrier™ 0414 Thermoplastic Olefin (TPO)
- Northstar Polymers MNB-013 Isocyanate Prepolymer
- Lucent Polymers PC/PBT-1212 Polycarbonate+PBT, General Purpose, Injection Grade
- Seals Eastern 7204 Ethylene-Propylene Rubber
- A. Schulman POLYBATCH™ Hot Sauce Red 50323/2 Concentrate Based In LLDPE
- DuPont Performance Polymers Delrin® FG900P NC010 Acetal (POM) (Unverified Data**)
- Arkema Group Pebax® MV 1041 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- Buckeye Polymers BP RPP 3005 GR BLK Polypropylene, Glass Filled
- Sumitomo Bakelite North America FS-80-P-1 Long-Glass Reinforced Diallyl Phthalate
Copyright © lookpolymers.com All Rights Reserved