Styron XU 73120.00 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | XU |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron XU 73120.00 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: XU 73120.00 Experimental Polycarbonate Resin is a high flow ignition resistant PC blend that contains no chlorinated or brominated additives. This resin is specifically designed to offer enhanced aesthetics and superior processing which makes it ideal for injection molding of large, thin-wall, or intricate parts. XU 73120.00 Experimental Polycarbonate Resin is suitable for use in a wide variety of applications in the Information Technology Equipment & Consumer Electronics industries. Applications:LCD TV Enclosures Monitor and PC EnclosuresInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.3 MPa @Thickness 3.20 mm |
9470 psi @Thickness 0.126 in |
Injection Molded; ASTM D638 |
| Tensile Strength, Yield | 64.8 MPa @Thickness 3.20 mm |
9400 psi @Thickness 0.126 in |
Injection Molded; ASTM D638 |
| Elongation at Break | 49 % @Thickness 3.20 mm |
49 % @Thickness 0.126 in |
Injection Molded; ASTM D638 |
| Tensile Modulus | 2.68 GPa @Thickness 3.20 mm |
389 ksi @Thickness 0.126 in |
Injection Molded; ASTM D638 |
| Flexural Strength | 95.1 MPa @Thickness 3.20 mm |
13800 psi @Thickness 0.126 in |
Injection Molded; ASTM D790 |
| Flexural Modulus | 2.70 GPa @Thickness 3.20 mm |
392 ksi @Thickness 0.126 in |
Injection Molded; ASTM D790 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.8 °C | 199 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 114 °C @Load 1.02 kg |
237 °F @Load 2.25 lb |
Rate B (120°C/h); ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
Black |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
All Colors |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 282 °C | 460 - 540 °F | |
| Mold Temperature | 37.8 - 87.8 °C | 100 - 190 °F | |
| Drying Temperature | 107 °C | 225 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Quadrant EPP Borotron® HM PE-HMW + boron based additive (ISO Data)
- PolyOne Geon™ Vinyl Flexible R5185A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Overview of materials for Nylon 12, 40% Glass Fiber Filled
- Kazanorgsintez PE2NT22-12 High Density Polyethylene Composite
- SABIC Innovative Plastics SABIC STAMAX 30YK270 PP
- Solvay Chemicals PHOSPHORIC ACID 80% - 87%
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
- Von Roll Isola IMI Varnish 708 Solventless Polyester Varnish for Electrical Insulation
- Chosun Refractories SM-1 Special Mortar
- 3M 99786NP Double Coated Tapes with 3M™ Adhesive 300MP
Copyright © lookpolymers.com All Rights Reserved