Solvay Technyl® C 206 Nylon 6, EH0
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C 206 Nylon 6, EH0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced Plyamide PA6, standard for fast cycling, for injection molding.Technyl C 206 has high fluidity and good mold release, favored by a high crystallization rate. It is specially suitable for the production of technical molding with fast injection cycles. This product is available in natural.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183-A |
| Water Absorption | 1.3 % | 1.3 % | 24 hours in water at 23°C; ISO 62. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 120 % | 120 % | ISO 527 |
| Tensile Modulus | 2.85 GPa | 413 ksi | ISO 527 |
| Flexural Yield Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Izod Impact Resistance | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
ISO 1210/UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
IEC 250 |
| Dissipation Factor | 0.023 @Frequency 1e+6 Hz |
0.023 @Frequency 1e+6 Hz |
IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 230 °C | 428 - 446 °F | |
| Middle Barrel Temperature | 225 - 235 °C | 437 - 455 °F | |
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-766B Epoxy Prepreg, 285 Kevlar® Reinforced
- PCC-Advanced Forming Technology 30% AlSiC Metal Matrix Composite
- Sylvin Technologies 9077-65 Natural PVC for Injection Molding
- Wellman Wellamid® GF1758-BK2 33% Glass Fiber Reinforced Nylon 66
- ExxonMobil Exceed™ 3512CB Film Resin
- Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (1 mm Molded Thickness)
- 3M AC-275 Class B-4 Aerospace Sealant
- BASF Neopolen® 1702 100 mm Expanded Polyethylene
- BASF Neopolen® P 8220 K 0.02 g/cc Core density; Expanded Polypropylene (Europe)
- ArcelorMittal 15 High formability steel for drawing, Hot rolled
Copyright © lookpolymers.com All Rights Reserved