Solvay Technyl® A238 Unfilled, Heat Stabilized, Impact Modified Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A238 Unfilled, Heat Stabilized, Impact Modified Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183-A |
| Water Absorption | 1.1 % | 1.1 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 2.55 GPa | 370 ksi | ISO 527 |
| Flexural Strength | 95.1 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263.0 °C | 505.4 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Middle Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Compression Zone |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Fill Speed | 300 - 600 mm/sec | 11.8 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 80 - 150 cm3/sec |
Users viewing this material also viewed the following:
- Polykemi AB SCANTEC PC S85R V0 Polycarbonate, Flame Retardant
- Premix Thermoplastics PRE-ELEC® ESD 1100 (discontinued **)
- Shandong Dongyue Polymer DF-302 PTFE Aqueous Dispersion 60%
- SSAB Tunnplat Aluzink 260A RP-X High-strength Metal-coated Steel
- SK Chemicals SKYPEL G355D Special Grade Flexibility-Resistant Grade
- Eagle Brass 304L Austenitic Stainless Steel, Annealed
- DuPont Performance Polymers Delrin® 100T NC010 Acetal (POM) (Unverified Data**)
- Arlon LW201Xxx-M1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Mylar Interleave
- A. Schulman POLYFORT™ FPP 2067HU UV Stabilized, High Heat Resistant Impact Polypropylene
- Overview of materials for Polyphenylene Sulfide (PPS), Unreinforced, Extruded
Copyright © lookpolymers.com All Rights Reserved