Solvay Technyl® A216V15 15% Glass Filled Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A216V15 15% Glass Filled Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183-A |
| Water Absorption | 1.1 % | 1.1 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125.0 MPa | 18130 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.98 kJ/m² | 2.85 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263.0 °C | 505.4 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Compression Zone |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Nozzle Temperature | 260 - 279 °C | 500 - 535 °F | |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-20064 P Urethane Foam, Very Soft, Supported with Clear Polyester Film
- Polimeri Europa Dutral® TER WO65 Ethylene - Propylene - Diene Terpolymer
- Lehmann & Voss LUVOCOM® 1105-7194/GY PEEK, unreinforced
- Karina 813D02/28-IS Yellow PVC Compound
- Polyram PlusTek PA840G13 Nylon 66 for Injection Molding, 13% Glass Fiber Reinforced, Impact Modified, Heat Resistant
- A. Schulman FORMION™ FI 395 Ionomer
- Chengdu Polyster H605 Thermoplastic Polyether-ester Elastomer (TPEE)
- Alliance Polymers Viprene™ G65A-32U-BLK Thermoplastic Vulcanizate Elastomer
- BASF Capron® GR30 HS 30% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Schmolz + Bickenbach Cryodur® 2363 (A-2) Cold Work Die Steel
Copyright © lookpolymers.com All Rights Reserved