- Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, DRY
Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYLSTAR™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL STAR Polyamide, reinforced with 35% of glass fiber, heat stabilized, for injection molding. Characterized by a high fluidity of the melt. Available in: Europe and North America Product Applications: Due to its outstanding flow characteristics, TECHNYL STAR S 218 V35 BLACK 31N provides a significant productivity improvement and allows more freedom in mould design and part design versus standard polyamide solutions. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183/A |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0053 cm/cm | 0.0053 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 10.7 GPa | 1550 ksi | ISO 527 Type 1A |
| Flexural Strength | 295 MPa | 42800 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180/1eA |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 225 °C | 428 - 437 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 225-235°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Ultem 1000M PEI
- Solvay Specialty Polymers Tecnoflon® FOR 5381 Fluoroelastomer
- UCAR Carbon UCAR® SF75 Extruded Graphite
- Toyobo PELPRENE™ S2004FS Polyester TPE, Flame Resistant
- ExxonMobil Exxon™ 2222 Regular Cure Rate Grade
- Compuestos Dominicanos Polycom AU-050595 PVC Compound
- Braskem LD7000A LDPE Blown Film Extrusion Polyethylene
- 3M 6035PC 12062 Polyurethane Foam Tape (20 lb./ft3 (320 kg/m3) Series)
- Austin Novel Materials Texalan® 698A Polyester and Polyether based TPU
- BASF Ecoflex® P BX 7020 Biodegradable Polyester
Copyright © lookpolymers.com All Rights Reserved