PolyOne Geon™ Vinyl Rigid Extrusion 87624 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87624 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 48.3 MPa | 7010 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.599 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 0.320 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.599 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| Dart Drop Total Energy | 50.3 J/cm @Temperature 23.0 °C |
0.0942 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 91.6 J/cm @Temperature 23.0 °C |
0.172 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C @Thickness 3.18 mm |
149 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 199 °C | 360 - 390 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Coextrusion | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Capstock | |
| Profiles | ||
| Vertical Blinds |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87727 Polyvinyl Chloride, Rigid (PVC, Rigid)
- PolyOne LubriOne™ NI-0920063 NATURAL Polyamide 610 (Nylon 610)
- LyondellBasell Petrothene® NA831000 Low Density Polyethylene
- Teknor Apex APEX® 1700-60 Polyvinyl Chloride, Flexible
- Tipco Tipcolite® TPF 1111 - Rubber & Mineral Modified Phenolic Resin, 19 mm Norton Flow with 7% Hexamine
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
- Arlon 19096R022 0.022" (0.559 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Braskem Symbios 4102 Polypropylene Terpolymer
- Ashley Polymers Ashlene® L935 Nylon 11
Copyright © lookpolymers.com All Rights Reserved