Solvay TECHNYL® C 246SI V30 PA6, 30% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 246SI V30 PA6, 30% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 6, reinforced with 30 % of glass fiber, with high impact resistance, for injection molding.Available in: Asia Pacific , Europe and North AmericaProduct Applications: Having good mechanical properties, this grade is used in all sectors of industry. This product is available in natural and black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183/A |
| Water Absorption | 0.88 % @Temperature 23.0 °C, Time 86400 sec |
0.88 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0084 cm/cm | 0.0084 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm | 0.0039 in/in | |
| 0.0084 cm/cm | 0.0084 in/in | ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0033 cm/cm | 0.0033 in/in | ISO 294-4 |
| 0.0046 cm/cm | 0.0046 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 Type 1A |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ISO 527 Type 1A |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 7.22 GPa | 1050 ksi | ISO 178 |
| Charpy Impact Unnotched | 9.20 J/cm² @Temperature 23.0 °C |
43.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.30 J/cm² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 260 °C | 482 - 500 °F | |
| Front Barrel Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 250-280°C |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_8310 Rigid Opaque Prototyping Polymer
- Huntsman PE1058 Film Extrusion Polyethylene (discontinued **)
- Petromont 2100 Medium Density Polyethylene Resin
- LG Chemical LUPOY EF5001RFT PC/ABS
- GrafTech GRAFOIL® GHW Standard Fluid Sealing Laminate, Non-Metal Reinforced
- Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C
- Bhansali Engineering Abstron SE-22M ABS Sheet Extrusion Grade
- Materion AlBeMet® AM 162 Rolled Sheet, Annealed
Copyright © lookpolymers.com All Rights Reserved