Solvay TECHNYL® C 218 V 50 PA6, 50% glass fiber, Eh 0
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 218 V 50 PA6, 50% glass fiber, Eh 0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL C 218 V50 is a polyamide 6 reinforced with 50% of glass fiber with excellent thermal stabilityColors: it is supplied in natural color and black color.Available in: Latin America and North AmericaMain Properties: ? Dimensional stability, Impact Resistance, Stiffness, and Excellent thermal resistance Applications: TECHNYL C 218 V50 is indicated for pieces that require dimensional stability and good mechanical proprieties like impact at higher temperatures.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183/A |
| Water Absorption | 0.75 % @Temperature 23.0 °C, Time 86400 sec |
0.75 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 225 MPa | 32600 psi | ISO R 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO R 527 |
| Tensile Modulus | 14.6 GPa | 2120 ksi | ISO R 527 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 10.7 J/cm² | 50.9 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
CEI 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 93 |
| Dielectric Constant | 3.8 | 3.8 | CEI 250 |
| Dissipation Factor | 0.020 | 0.020 | CEI 250 |
| Comparative Tracking Index | 550 V | 550 V | CEI 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Nozzle Temperature | 230 - 240 °C | 446 - 464 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C | |
| Mixing Zone | 240-250°C |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7640-1 (Natural) Thermoplastic Elastomer (TPE)
- STAR Thermoplastic Alloys & Rubbers StarGrip GP 45-9000 TPE
- Zeon Chemicals Sivic® Z730 Polyblend Nitrile Elastomer
- Lubrizol ESTANE® 58881 Ether Based Thermoplastic Polyurethane (European Grade)
- Vyncolit 2920 W Novolac Phenolic
- Fainplast Compounds Hax™ HFC 0108/4 Flame Retardant Polyolefin Cable Compound
- Amco PRIMATOP HDPE RP 004 Granular High Density Polyethylene
- Pyrotek Pyrocast PT-60 Castable Refractory
- Hexion Bakelite™ PF 2874 Phenolic Formaldehyde Resin, Low Shrinkage, Improved Electrical Properties, UL Listed, High Mechanical Strength
- Polimeri Europa SINKRAL H220 ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved