UBE PAE1200U Nylon Elastomer
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | UBE |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE PAE1200U Nylon Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBESTA Nylon 12 ElastomerInformation provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 235 °C |
14 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 | 58 | |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Flexural Strength | 7.00 MPa | 1020 psi | ASTM D790 |
| Flexural Modulus | 0.150 GPa | 21.8 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 154 °C | 309 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Injection Molding |
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
| Compression Ratio | 2.5-3.5:1 | Injection Molding |
| min 3:1 | For 8x1 mm Tube Extrusion | |
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
| Die Width | 300 mm | For T-Die Cast Film Extrusion |
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
| Flight Depth in the Feeding Zone | 10-15% of Screw Diameter | Injection Molding |
| Flight Depth in the Metering Zone | 5-7% of Screw Diameter | Injection Molding |
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
| min 20:1 | Injection Molding | |
| Length of Compression Zone | 25-45% of total screw length | Injection Molding |
| 30% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Feeding Zone | 20-40% of total screw length | Injection Molding |
| 30-40% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
| 35-45% of total screw length | Injection Molding | |
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
| Peripheral screw speed | 10 m/min | Injection Molding |
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir RK Polystyrene (discontinued **)
- Kaiser 6033 T8 Rod & Bar
- Indium Corp. Indalloy® 239 Pb-Ag-Sn-In Solder Alloy
- Shuman 780H Grey ABS
- Plenco 7487 Phenolic, Granular, Transfer Molded
- Unifrax Fiberfrax® Bulk 7000 High Purity Bulk Fiber
- EMS-Griltech Grilon® XC 130 Nylon 610 Monofilament (Non-Set)
- DuPont Teijin Films Mylar® WRL63 Polyester Film, 200 Gauge
- Arlon LW202Txx-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- Axiall 7055 Rigid PVC, Extrusion, White
Copyright © lookpolymers.com All Rights Reserved