Solvay TECHNYL® A 221 Natural FA PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 221 Natural FA PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Product in development. Unreinforced polyamide 66, medium viscosity, for injection molding, with a special crystallizing agent, for fast cycles. Suitable for food contact applicationsAvailable in: Europe and North AmericaProduct Applications: TECHNYL® A 221 NATURAL FA offers a good combination between primary properties of the unreinforced polyamide 66 and processing properties leading to increased productivity. These performances are associated with excellent dimensional stability and good rigidity of molded parts. This grade is used in a wide variety of industries: Automotive: connectors, Electrical: connectors, rotary switches and Consumer goods: lighters, aerosol valves. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage | 0.0082 cm/cm | 0.0082 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0127 cm/cm | 0.0127 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0155 cm/cm | 0.0155 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 Type 1A |
| Elongation at Break | 20 % | 20 % | ISO 527 Type 1A |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 Type 1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.250 J/cm² @Temperature 23.0 °C |
1.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-280°C |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE G 7410 NAT
- SABIC Innovative Plastics Lexan® LCG2007 PC (Asia Pacific)
- ExxonMobil LD 146.NH Cast Film Resin (discontinued **)
- Mi-Tech Metals TC70 70 Tungsten Carbide/30 Copper PM Metal Composite
- LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced
- Techmer ES HiFill® POM CO GC20 20% Glass Bead Filled
- Westlake Plastics Pomalux® Acetal Copolymer For Medical Applications
- Polyram RamSter PF810 PBT, Impact Modified
- DuPont Performance Polymers Crastin® CE2055 BK580 Polybutylene Terephthalate (PBT)
- Fainplast Compounds GS 54 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved