- Solvay TECHNYL® A 218 V40 Black 21 NHFE PA66, 40% glass fiber, DRY
Solvay TECHNYL® A 218 V40 Black 21 NHFE PA66, 40% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 V40 Black 21 NHFE PA66, 40% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, offering high flowability and productivity gains, reinforced with 40% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL ® A 218 V40 BLACK 21NHFE is characterized by a high flowability and offers an excellent combination between thermal and mechanical properties. This grade is ideal for use in the automotive industry for engine components, such as: inlet manifolds, air ducts - engine covers, and various housings and liquid containers. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 220 MPa | 31900 psi | ISO 527 Type 1A |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 Type 1A |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527 Type 1A |
| Flexural Strength | 305 MPa | 44200 psi | ISO 178 |
| Flexural Modulus | 10.8 GPa | 1570 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.5 kJ/m² | 6.42 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 9.70 J/cm² | 46.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FT-2481 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Hyosung Topilene C600H PP
- Michelman® Michem® Lube 188F Anionic carnauba/paraffin wax emulsion
- Sibur SKI-3S 1st Grade, 2nd Group Isoprene Rubber (IR)
- Polyram PlusTek RA102 Nylon 6.6, General Purpose
- A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
- Cyclewood Solutions Xylomer™ XM1-KJD Injection Molding Compostable Resin
- DuPont™ Surlyn® 8140 Ionomer Resin, Sodium
- Entec Hypro™ PPH-T20 Homopolymer Polypropylene, 20% Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved