SABIC Innovative Plastics LNP VERTON RV00AE PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00AE PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RV00AE is a compound based on Nylon 66 containing 50% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.640 % | 0.640 % | 50% RH, 24 hrs; ASTM D570 |
| 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 216 MPa | 31300 psi | 5 mm/min; ISO 527 |
| 219 MPa | 31800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 14.45 GPa | 2096 ksi | 1 mm/min; ISO 527 |
| 15.66 GPa | 2271 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 342 MPa | 49600 psi | ISO 178 |
| 359 MPa | 52100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 362 MPa | 52500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.31 GPa | 1930 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.92 J/cm | 7.34 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.6 J/cm | 23.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 83.0 kJ/m² | 39.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 74.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 226 °C @Thickness 3.20 mm |
439 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GA-2285FR PVC
- Polykemi AB POLYfill PP CIM9040 Polypropylene, Mineral Reinforced
- Solvay Specialty Polymers Udel® P-3700 HC Polysulfone (PSU) (Unverified Data**)
- 3M Dyneon™ TFM™ 1705 Modified PTFE Powder (discontinued **)
- High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C)
- Latrobe DuraTechâ„¢ M4 Powder Metal High Speed Steel (ASTM M4)
- Hexcel® HexWeb® HRH-78 - 1/8 - 3.0 Commercial Grade Nomex Honeycomb/Phenolic Resin
- A. Schulman POLYBATCH™ Ivory 90034/4 Concentrate Based In LDPE
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Iceberg Clay Filler
- ChevronTexaco Canopus® 100
Copyright © lookpolymers.com All Rights Reserved