- Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, DRY
Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA66, reinforced with 20% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 218 V20 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is commonly used in the automotive industry for engine components, such as: air ducts and various liquid containers. This product is available in natural, black and grey.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183/A |
| Water Absorption | 1.0 % @Temperature 23.0 °C, Time 86400 sec |
1.0 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 Type 1A |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 Type 1A |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ISO 527 Type 1A |
| Flexural Modulus | 6.40 GPa | 928 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
Ignition Temperature; ISO 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Michelman® SofTak® 317 Non-skid coating
- SABIC Innovative Plastics ULTEM AR9100 PEI (Asia Pacific)
- Shin-Etsu Silicones KE-3417 Silicone, RTV Adhesive
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Hexcel® HexWeb® HRH-10 - 1/8- 3.0 Aramid Fiber/Phenolic Resin Honeycomb
- Eastman Sahara Film
- DuPont Performance Polymers Crastin® SK642FR NC010 Polybutylene Terephthalate (PBT)
- Ashley Polymers Ashlene® 527LD-45LG Nylon 66, 45% Long Glass Fiber Reinforced
- A. Schulman POLYBATCH™ Norwegian Wood 60242U/3 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved