AK Steel NITRONIC® 30 Austenitic Stainless Steel

Category Metal , Ferrous Metal , Stainless Steel
Manufacturer AK Steel
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF AK Steel NITRONIC® 30 Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combined with good toughness and economy. Specific potential applications include automotive hose clamps, safety belt anchors, truck and bus frames, water supply and control structures, sewage treatment plant structures, bulk solids handling equipment, magnetic ore separator screens, coal buckets and hopper cars. Stainless steels have served successfully in many structural components in the transportation industry. Bus space frames and bumpers take advantage of the excellent fabricability and high strength and toughness of stainless steel. Tensilized NITRONIC 30 Stainless Steel has been used in rapid transit structurals where the strength-to-weight ratio of up to three times that of carbon steel has improved operating efficiency. Rear frames of refrigerated trucks are easily welded and formed from NITRONIC 30 Stainless Steel, resulting in protective units that can withstand impact blows without cracking. Shipboard container structurals use stainless steel successfully where carbon steel becomes scuffed and rusts wherever the paint is damaged. AK Steel NITRONIC 30 is a nitrogen-strengthened stainless steel developed for applications requiring a good level of aqueous corrosion resistance combined with good toughness and economy. AK Steel NITRONIC 30 Stainless Steel provides approximately 50% higher yield strength than Type 304L and, therefore, may allow lighter gauges to further reduce costs. AK Steel NITRONIC 30 Stainless Steel work hardens rapidly while retaining good ductility. Unlike other nitrogen-strengthened stainless steels, AK Steel NITRONIC 30 Stainless Steel is subject to magnetic transformation when cold worked.Information provided by AK Steel
Mechanical Properties Metric English Comments
Hardness, Rockwell B 95
95
0% Cold Work
92.5
<br>@Temperature 23.9 °C
 92.5
<br>@Temperature 75.0 °F
 Plate
96.5
<br>@Temperature 23.9 °C
 96.5
<br>@Temperature 75.0 °F
92
<br>@Thickness 22.2 mm
 92
<br>@Thickness 0.875 in
 Typical for Plate, Annealed, in 2&quot;
93
<br>@Thickness 1.63 mm
 93
<br>@Thickness 0.0640 in
 Annealed at 2050°F, Longitudinal
93
<br>@Thickness 1.63 mm
 93
<br>@Thickness 0.0640 in
 Annealed at 2050°F, Transverse
93.5
<br>@Thickness 3.15 mm
 93.5
<br>@Thickness 0.124 in
 Annealed at 1950°F, Longitudinal
94
<br>@Thickness 0.813 mm
 94
<br>@Thickness 0.0320 in
 Annealed at 1950°F, Longitudinal
94
<br>@Thickness 0.813 mm
 94
<br>@Thickness 0.0320 in
 Annealed at 1950°F, Longitudinal
94
<br>@Thickness 9.52 mm
 94
<br>@Thickness 0.375 in
 Typical for Plate, Annealed
Hardness, Rockwell C 31
31
10% Cold Work
37
37
20% Cold Work
43
43
30% Cold Work
45
45
40% Cold Work
33.5
<br>@Thickness 4.762 mm
 33.5
<br>@Thickness 0.1875 in
 Typical for Plate, 1/4-Hard, Longitudinal
33.5
<br>@Thickness 4.762 mm
 33.5
<br>@Thickness 0.1875 in
 Typical for Plate, 1/4-Hard, Transverse
34
<br>@Thickness 6.35 mm
 34
<br>@Thickness 0.250 in
 Typical for Plate, 1/4-Hard, Longitudinal
34
<br>@Thickness 6.35 mm
 34
<br>@Thickness 0.250 in
 Typical for Plate, 1/4-Hard, Transverse
Tensile Strength, Ultimate 862 MPa
125000 psi
0% Cold Work
1034 MPa
150000 psi
10% Cold Work
1193 MPa
173000 psi
20% Cold Work
1338 MPa
194100 psi
30% Cold Work
1467 MPa
212800 psi
40% Cold Work
417 MPa
<br>@Temperature 538 °C
 60500 psi
<br>@Temperature 1000 °F
 Plate
439 MPa
<br>@Temperature 482 °C
 63700 psi
<br>@Temperature 900 °F
 Plate
459 MPa
<br>@Temperature 538 °C
 66500 psi
<br>@Temperature 1000 °F
 Sheet
460 MPa
<br>@Temperature 427 °C
 66700 psi
<br>@Temperature 800 °F
 Plate
480 MPa
<br>@Temperature 371 °C
 69600 psi
<br>@Temperature 700 °F
 Plate
485 MPa
<br>@Temperature 482 °C
 70300 psi
<br>@Temperature 900 °F
 Sheet
487 MPa
<br>@Temperature 260 °C
 70600 psi
<br>@Temperature 500 °F
 Plate
488 MPa
<br>@Temperature 316 °C
 70800 psi
<br>@Temperature 600 °F
 Plate
496 MPa
<br>@Temperature 204 °C
 71900 psi
<br>@Temperature 400 °F
 Plate
506 MPa
<br>@Temperature 427 °C
 73400 psi
<br>@Temperature 800 °F
 Sheet
529 MPa
<br>@Temperature 371 °C
 76700 psi
<br>@Temperature 700 °F
 Sheet
539 MPa
<br>@Temperature 149 °C
 78200 psi
<br>@Temperature 300 °F
 Plate
547 MPa
<br>@Temperature 316 °C
 79300 psi
<br>@Temperature 600 °F
 Sheet
547 MPa
<br>@Temperature 260 °C
 79300 psi
<br>@Temperature 500 °F
 Sheet
561 MPa
<br>@Temperature 204 °C
 81400 psi
<br>@Temperature 400 °F
 Sheet
598 MPa
<br>@Temperature 149 °C
 86800 psi
<br>@Temperature 300 °F
 Sheet
630 MPa
<br>@Temperature 93.3 °C
 91400 psi
<br>@Temperature 200 °F
 Plate
692 MPa
<br>@Temperature 93.3 °C
 100000 psi
<br>@Temperature 200 °F
 Sheet
845 MPa
<br>@Temperature 23.9 °C
 123000 psi
<br>@Temperature 75.0 °F
 Sheet
850 MPa
<br>@Temperature 23.9 °C
 123000 psi
<br>@Temperature 75.0 °F
 Plate
689 MPa
<br>@Thickness 1.63 mm
 99900 psi
<br>@Thickness 0.0640 in
 Annealed at 2050°F, Longitudinal
711 MPa
<br>@Thickness 1.63 mm
 103000 psi
<br>@Thickness 0.0640 in
 Annealed at 2050°F, Transverse
786 MPa
<br>@Thickness 9.52 mm
 114000 psi
<br>@Thickness 0.375 in
 Typical for Plate, Annealed
811 MPa
<br>@Thickness 3.15 mm
 118000 psi
<br>@Thickness 0.124 in
 Annealed at 1950°F, Longitudinal
825 MPa
<br>@Thickness 0.813 mm
 120000 psi
<br>@Thickness 0.0320 in
 Annealed at 1950°F, Longitudinal
827 MPa
<br>@Thickness 50.8 mm
 120000 psi
<br>@Thickness 2.00 in
 Typical for Plate, Annealed
840 MPa
<br>@Thickness 0.813 mm
 122000 psi
<br>@Thickness 0.0320 in
 Annealed at 1950°F, Longitudinal
855 MPa
<br>@Thickness 22.2 mm
 124000 psi
<br>@Thickness 0.875 in
 Typical for Plate, Annealed
998 MPa
<br>@Thickness 6.35 mm
 145000 psi
<br>@Thickness 0.250 in
 Typical for Plate, 1/4-Hard, Longitudinal
1011 MPa
<br>@Thickness 6.35 mm
 146600 psi
<br>@Thickness 0.250 in
 Typical for Plate, 1/4-Hard, Transverse
1020 MPa
<br>@Thickness 4.762 mm
 148000 psi
<br>@Thickness 0.1875 in
 Typical for Plate, 1/4-Hard, Longitudinal
1025 MPa
<br>@Thickness 4.762 mm
 148700 psi
<br>@Thickness 0.1875 in
 Typical for Plate, 1/4-Hard, Transverse
Tensile Strength, Yield 345 MPa
<br>@Strain 0.200 %
 50000 psi
<br>@Strain 0.200 %
 Typical for Plate, Annealed, 0.875&quot;
358 MPa
<br>@Strain 0.200 %
 51900 psi
<br>@Strain 0.200 %
 Typical for Plate, Annealed, 2&quot;
393 MPa
<br>@Strain 0.200 %
 57000 psi
<br>@Strain 0.200 %
 Typical for Plate, Annealed, 0.0375&quot;
393 MPa
<br>@Strain 0.200 %
 57000 psi
<br>@Strain 0.200 %
 0% Cold Work
593 MPa
<br>@Strain 0.200 %
 86000 psi
<br>@Strain 0.200 %
 10% Cold Work
702 MPa
<br>@Strain 0.200 %
 102000 psi
<br>@Strain 0.200 %
 Typical for Plate, 1/4-Hard, Longitudinal, 0.25&quot;
717 MPa
<br>@Strain 0.200 %
 104000 psi
<br>@Strain 0.200 %
 Typical for Plate, 1/4-Hard, Longitudinal, 0.1875'
759 MPa
<br>@Strain 0.200 %
 110000 psi
<br>@Strain 0.200 %
 Typical for Plate, 1/4-Hard, Transverse, 0.25&quot;
768 MPa
<br>@Strain 0.200 %
 111000 psi
<br>@Strain 0.200 %
 Typical for Plate, 1/4-Hard, Transverse, 0.1875&quot;
779 MPa
<br>@Strain 0.200 %
 113000 psi
<br>@Strain 0.200 %
 20% Cold Work
979 MPa
<br>@Strain 0.200 %
 142000 psi
<br>@Strain 0.200 %
 30% Cold Work
1186 MPa
<br>@Strain 0.200 %
 172000 psi
<br>@Strain 0.200 %
 40% Cold Work
131 MPa
<br>@Strain 0.200 %,<br> Temperature 538 °C
 19000 psi
<br>@Strain 0.200 %,<br> Temperature 1000 °F
 Plate
155 MPa
<br>@Strain 0.200 %,<br> Temperature 482 °C
 22500 psi
<br>@Strain 0.200 %,<br> Temperature 900 °F
 Plate
157 MPa
<br>@Strain 0.200 %,<br> Temperature 427 °C
 22800 psi
<br>@Strain 0.200 %,<br> Temperature 800 °F
 Plate
168 MPa
<br>@Strain 0.200 %,<br> Temperature 371 °C
 24400 psi
<br>@Strain 0.200 %,<br> Temperature 700 °F
 Plate
174 MPa
<br>@Strain 0.200 %,<br> Temperature 316 °C
 25200 psi
<br>@Strain 0.200 %,<br> Temperature 600 °F
 Plate
182 MPa
<br>@Strain 0.200 %,<br> Temperature 260 °C
 26400 psi
<br>@Strain 0.200 %,<br> Temperature 500 °F
 Plate