LyondellBasell Lupolen® 6021 D HDPE, Blow Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 6021 D HDPE, Blow Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flow, blow molding grade for small, rigid, thin-walled containers (up to 5 l), pots (up to 1 l), bottles and canisters (up to 5 l) for packaging mineral oil, antifreeze, brake fluid; drink bottles, handled containers (up to 6 l), etc.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | |
| Melt Flow | 0.265 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.265 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| Tensile Modulus | 1.40 GPa | 203 ksi | |
| Tensile Impact Strength | 120 kJ/m² | 57.1 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 510 MPa | 74000 psi | |
| Tensile Creep Modulus, 1000 hours | 340 MPa | 49300 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | |
| Vicat Softening Point | 80.0 °C | 176 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Permabond LH050 Anaerobic Threadsealant
- Lotus Nano Paint NAX 01 Tow-Component Nano-paint
- Hong Kun Group 4-Fluoro-3-methylacetophenone Pharmaceutical Intermediate
- SABIC Innovative Plastics NORYL SA120FIN PPE
- Styron XZ 97222.00 SB Latex
- ChevronTexaco Transultex® D
- China Tungsten YG3 Tungsten Carbide for Cutting Tools
- Eurofoam Porocell POR 304 CM-BI EPDM Foam
- Bhansali Engineering Santron IMS 2000 Glitter SAN Resin
- Arlon R38041X012 0.012" (0.305 mm) Uncured Fluorosilicone with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved