SABIC Innovative Plastics LNP STAT-KON QE002S PA6.10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON QE002S PA6.10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* QE002S is a compound based on Nylon 6/10 containing 10% carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.280 % | 0.280 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 142 MPa | 20600 psi | 5 mm/min; ISO 527 |
| 143 MPa | 20700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 144 MPa | 20900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.37 GPa | 1210 ksi | 1 mm/min; ISO 527 |
| 8.48 GPa | 1230 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 195 MPa | 28300 psi | ISO 178 |
| 197 MPa | 28600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 201 MPa | 29200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.72 GPa | 975 ksi | 2 mm/min; ISO 178 |
| 7.16 GPa | 1040 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.77 J/cm | 8.94 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-CL(6) 6 MFI Clear Polycarbonate with Release
- Solvay Specialty Polymers Solef® 42308 Polyvinylidene Fluoride (PVDF)
- ChevronTexaco 150 PMO Premium
- DSM Arnitel® EM400-BP TPC-ET
- Dow CYCLOTENE™ 4022-35 Advanced Electronic Resins (PhotoBisbenzocyclobutene BCB)
- Amco Amalloy® B9336 Polymer Alloy
- Arkema Group Rilsan® MB 3000 Nylon 11, Sheathing Grade (Conditioned)
- Shinkong Synthetic Fibers Shinite® D201G30 PBT, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved