Solvay Specialty Polymers RytonÂ® R-4-220NA Polyphenylene Sulfide (PPS), 40% Glass Fiber

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer	Solvay Specialty Polymers
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers RytonÂ® R-4-220NA Polyphenylene Sulfide (PPS), 40% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

RytonÂ® R-4-220NA and R-4-220BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength after constant or repeated exposure to high temperature water.Features: Good StrengthAdditional Properties: Hydrolytic Stability - > 80 %; Hydrolytic Stability - < 1.0 %Automotive Specifications CHRYSLER MS-DB-570 CPN4241 Color: Natural; FORD WSL-M4D807-A; GM GMP.PPS.001Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.68 g/cc	0.0607 lb/inÂ³	ASTM D792
Filler Content	40 %	40 %	Glass Fiber
Water Absorption	0.020 % @Time 86400 sec	0.020 % @Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm @Thickness 3.18 mm	0.0020 in/in @Thickness 0.125 in
Linear Mold Shrinkage, Transverse	0.0050 cm/cm @Thickness 3.20 mm	0.0050 in/in @Thickness 0.126 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	103	103	ASTM D785
Hardness, Rockwell R	122	122	ASTM D785
Tensile Strength	186 MPa	27000 psi	ASTM D638
Tensile Stress	190 MPa	27600 psi	ISO 527-2
Elongation at Break	1.6 %	1.6 %	ISO 527-2
	1.6 %	1.6 %	ASTM D638
Flexural Strength	269 MPa	39000 psi	ASTM D790
	275 MPa	39900 psi	ISO 178
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
	14.5 GPa	2100 ksi	ASTM D790
Compressive Strength	275 MPa	39900 psi	ASTM D695
Poissons Ratio	0.37	0.37	ASTM E132
Izod Impact, Notched	0.910 J/cm @Thickness 3.18 mm	1.70 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	6.40 J/cm @Thickness 3.18 mm	12.0 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	9.00 kJ/mÂ²	4.28 ft-lb/inÂ²	Notch A; ISO 180
Izod Impact, Unnotched (ISO)	35.0 kJ/mÂ²	16.7 ft-lb/inÂ²	ISO 180

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 Âµm/m-Â°C @Temperature 100 - 200 Â°C	8.33 Âµin/in-Â°F @Temperature 212 - 392 Â°F	2
	15.0 Âµm/m-Â°C @Temperature -50.0 - 50.0 Â°C	8.33 Âµin/in-Â°F @Temperature -58.0 - 122 Â°F	2
CTE, linear, Transverse to Flow	40.0 Âµm/m-Â°C @Temperature -50.0 - 50.0 Â°C	22.2 Âµin/in-Â°F @Temperature -58.0 - 122 Â°F	TMA; ASTM E831
	85.0 Âµm/m-Â°C @Temperature 100 - 200 Â°C	47.2 Âµin/in-Â°F @Temperature 212 - 392 Â°F	TMA; ASTM E831
Thermal Conductivity	0.310 W/m-K	2.15 BTU-in/hr-ftÂ²-Â°F	ASTM C177
Maximum Service Temperature, Air	200 - 220 Â°C	392 - 428 Â°F	UL Temperature Rating
Deflection Temperature at 1.8 MPa (264 psi)	265 Â°C	509 Â°F	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
Oxygen Index	45 %	45 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Constant	3.8 @Frequency 1000 Hz	3.8 @Frequency 1000 Hz	ASTM D150
	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	22.0 kV/mm	559 kV/in	ASTM D149
Dissipation Factor	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz	ASTM D150
	0.0030 @Frequency 1.00e+6 Hz	0.0030 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	125 sec	125 sec	ASTM D495
Comparative Tracking Index	150 V	150 V	UL 746

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	Latin America
	North America
Color	Natural
Form	Pellets
Processing Technique	Injection Molding
RoHS Compliance	RoHS Compliant