BASF Ultramid® A3EG6 30% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3EG6 30% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 5.2 - 5.8 % | 5.2 - 5.8 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 - 1.9 % | 1.5 - 1.9 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 145 cm³/g | 145 cm³/g | Viscosity number; ISO 307 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 54.4 g/10 min @Load 5.00 kg, Temperature 275 °C |
54.4 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 130 MPa | 18900 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 7.20 GPa | 1040 ksi | ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.5 kJ/m² | 7.38 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 5300 MPa | 769000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 260 °C | 500 °F | DIN 53765 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20,000 hr |
| 165 °C | 329 °F | for 50% loss of tensile strength after 5,000 hr | |
| 240 °C | 464 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 5.6 @Frequency 1.00e+6 Hz |
5.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz |
0.16 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| FDA | 21 CFR 177.1500 | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® MR 80 High Density Polyethylene - Injection Molding
- Premix Premi-Glas® 3101-10 Fiberglass Reinforced Thermoset BMC
- Mo-Sci Corporation GL-0191 Soda-Lime Glass Spheres
- DuPont Elvax® 3185 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion
- Tisan TISLAMID® 6 30% Glass Filled Impact Modified Nylon 6
- Wellman Wellamid® GF30-60 XE-WBK Nylon 6, 30% Glass Reinforced, Weatherable
- Chosun Refractories CH-1 Hard Fireclay brick
- Bulk Molding Compounds BMC A50-XHS High Strength Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved