Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ketaspire KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear resistance, this grade offers high lubricity while retaining outstanding ductility and toughness that surpasses that of unmodified high viscosity PEEK. Also, this product offers high melt flow, which allows injection molding of thin, intricate, or complex parts. In addition to these differentiating features, this resin also offers the outstanding combination of ultra-performance attributes commonly known for PEEK. These include: mechanical strength and stiffness even at elevated temperatures, long term thermal-oxidative stability, fatigue resistance, and excellent chemical resistance to a broad range of harsh chemical environments including acids, bases, and organics. The attractive combination of properties make Ketaspire KT-820 SL10 suitable for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Viscosity 170 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
170 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt; ASTM D3835
Linear Mold Shrinkage, Flow 0.012 - 0.014 cm/cm

@Thickness 3.20 mm
0.012 - 0.014 in/in

@Thickness 0.126 in
5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse 0.016 - 0.018 cm/cm

@Thickness 3.20 mm
0.016 - 0.018 in/in

@Thickness 0.126 in
5" x 0.5" x 0.125" bar; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore D 83

@Time 1.00 sec
83

@Time 0.000278 hour
ASTM D2240
Tensile Strength 88.0 MPa
12800 psi
50 mm/min; ASTM D638
Elongation at Break 60 %
60 %
50 mm/min; ASTM D638
60 %
60 %
ISO 527-2/1A/50
Elongation at Yield 5.2 %
5.2 %
50 mm/min; ASTM D638
Tensile Modulus 3.60 GPa
522 ksi
50 mm/min; ASTM D638
Flexural Strength 134 MPa
19400 psi
ASTM D790
Flexural Yield Strength 134 MPa
19400 psi
ASTM D790
Flexural Modulus 3.50 GPa
508 ksi
ASTM D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
NB
NB
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Annealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 365 °C
689 °F
Middle Barrel Temperature 370 °C
698 °F
Front Barrel Temperature 375 °C
707 °F
Nozzle Temperature 380 °C
716 °F
Mold Temperature 175 - 205 °C
347 - 401 °F
Drying Temperature 150 °C
302 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Wear Resistance
High Heat Resistance
Forms Pellets
Generic PEEK
Injection Rate Fast
Processing Method Injection Molding
Machining
Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.5:1.0 to 3.5:1.0
Uses Film
Industrial Applications
Oil/Gas Applications
Profiles
Rods
Sheet
Tubing