- Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA), 50% Glass Fiber
Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA), 50% Glass Fiber
| Category | Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC) |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Ixef® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA), 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ixef® 1521 is a 50% glass-fiber reinforced, flame retardant polyarylamide which exhibits high strength and stiffness, outstanding surface gloss, and excellent creep resistance.Features: Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; High Flow; High Strength; Low Moisture Absorption; Outstanding Surface Finish; Ultra High StiffnessUses: Aircraft Applications; Appliance Components; Appliances; Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bushings; Business Equipment; Camera Applications; Furniture; Gears; Industrial Applications; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Additional Properties: Moisture Absorption - Internal Method 1.3 %Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ISO 1183 |
| Filler Content | 50 % | 50 % | Glass Fiber |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527-2 |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527-2 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527-2 |
| Flexural Strength | 340 MPa | 49300 psi | ISO 178 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ISO 178 |
| Izod Impact, Notched | 0.950 J/cm | 1.78 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C | 9.44 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | V-0 @Thickness 0.750 - 1.50 mm |
V-0 @Thickness 0.0295 - 0.0591 in |
|
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
||
| Oxygen Index | 32 % | 32 % | ISO 4589-2 |
| Glow Wire Test | 900 °C @Thickness 3.00 mm |
1650 °F @Thickness 0.118 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 |
| 900 °C @Thickness 0.800 mm |
1650 °F @Thickness 0.0315 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
| 930 °C @Thickness 1.50 mm |
1710 °F @Thickness 0.0591 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Glow Wire Flammability Index, IEC 60695-2-12 | |
| 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
Glow Wire Flammability Index, IEC 60695-2-12 | |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index, IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IIEC 60093 |
| Dielectric Constant | 4.1 @Frequency 1.10e+8 Hz |
4.1 @Frequency 1.10e+8 Hz |
IEC 60250 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.012 @Frequency 110 Hz |
0.012 @Frequency 110 Hz |
IEC 60250 |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Front Barrel Temperature | 260 - 290 °C | 500 - 554 °F | |
| Melt Temperature | 270 °C | 518 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 120 °C @Time 1800 - 5400 sec |
248 °F @Time 0.500 - 1.50 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Flame Retardant | |
| Agency Ratings | FAA FAR 25.853a | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Colors; Natural | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir RCL 600 Polystyrene (discontinued **)
- Kazanorgsintez Carbanox SKD-10 Polyethyleneglycol Mixture
- Kinlead HSD11 Normal Grade Heat Sealable Film (thickness: 18 µm)
- Karina 801-27/13-IS-RG Smoky Clear PVC Compound
- Henkel Turco Metal Glo FF Jet Metal Brightener
- Tra-Con Tra-Bond F125 Fast Gel Clear Epoxy Adhesive
- Diamond Polymers ABS/PC FC-30
- Arlon 51112R013 0.013" (0.330 mm) Cured, Self Fusing, Silicone Rubber with Fiberglass Substrate
- Arlon 99322B015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Akzo Nobel Expancel® 950 DU 120 Dry unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved