Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AvaSpire AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This resin retains most of the desirable ultra-performance attributes of glass reinforced PEEK, including chemical resistance, fatigue resistance and long term thermal oxidative stability, but the heat deflection temperature is lower than 30% GF PEEK. The material's excellent balance of properties makes it well suited for demanding applications across a broad range of industries including healthcare, transportation, electronics, oil and gas, and chemical processing. - Beige: AV-621 GF30 BG 20 - Black: AV-621 GF30 BK95Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Specific Gravity	1.55 g/cc	1.55 g/cc	ASTM D792
Filler Content	30 %	30 %	Glass Fiber Reinforcement
Water Absorption	0.20 % @Time 86400 sec	0.20 % @Time 24.0 hour	ASTM D570
Viscosity	650000 cP @Shear Rate 1000 1/s, Temperature 400 °C	650000 cP @Shear Rate 1000 1/s, Temperature 752 °F	Melt; ASTM D3835
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.18 mm	0.0010 - 0.0030 in/in @Thickness 0.125 in	5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Thickness 3.18 mm	0.0090 - 0.011 in/in @Thickness 0.125 in	5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 400 °C	2.0 g/10 min @Load 4.76 lb, Temperature 752 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	101	101	M-Scale; ASTM D785
Tensile Strength	147 MPa	21300 psi	5.0 mm/min; ASTM D638
Tensile Strength, Yield	158 MPa	22900 psi	ISO 527-2/1A/5
Elongation at Break	3.2 %	3.2 %	5.0 mm/min; ASTM D638
	3.2 %	3.2 %	ISO 527-2/1A/5
Tensile Modulus	9.90 GPa	1440 ksi	5.0 mm/min; ASTM D638
	10.6 GPa	1540 ksi	ISO 527-2/1A/1
Flexural Strength	236 MPa	34200 psi	ISO 178
	237 MPa	34400 psi	ASTM D790
Flexural Modulus	9.40 GPa	1360 ksi	ASTM D790
	9.80 GPa	1420 ksi	ISO 178
Compressive Strength	159 MPa	23100 psi	ASTM D695
Poissons Ratio	0.43	0.43	ASTM E132
Shear Modulus	3.46 - 3.71 GPa	502 - 538 ksi	Calculated
Shear Strength	84.5 MPa	12300 psi	ASTM D732
Izod Impact, Notched	1.20 J/cm	2.25 ft-lb/in	ASTM D256
	10.0 J/cm	18.7 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	14.0 kJ/m²	6.66 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	70.0 kJ/m²	33.3 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	17.0 µm/m-°C @Temperature -50.0 - 50.0 °C	9.44 µin/in-°F @Temperature -58.0 - 122 °F	TMA; ASTM E831
Specific Heat Capacity	1.29 J/g-°C @Temperature 50.0 °C	0.308 BTU/lb-°F @Temperature 122 °F	DSC
	1.66 J/g-°C @Temperature 200 °C	0.397 BTU/lb-°F @Temperature 392 °F	DSC
Thermal Conductivity	0.280 W/m-K	1.94 BTU-in/hr-ft²-°F	ASTM E1530
Melting Point	340 °C	644 °F	Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	217 °C	423 °F	Annealed; ASTM D648
Glass Transition Temp, Tg	158 °C	316 °F	ASTM D3418
Flammability, UL94	V-1 @Thickness 0.800 mm	V-1 @Thickness 0.0315 in	UL 94
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.10e+17 ohm-cm	2.10e+17 ohm-cm	ASTM D257
Surface Resistance	>= 1.90e+17 ohm	>= 1.90e+17 ohm	ASTM D257
Dielectric Constant	3.48 @Frequency 1.00e+6 Hz	3.48 @Frequency 1.00e+6 Hz	ASTM D150
	3.52 @Frequency 60.0 Hz	3.52 @Frequency 60.0 Hz	ASTM D150
	3.53 @Frequency 1000 Hz	3.53 @Frequency 1000 Hz	ASTM D150
Dielectric Strength	15.0 kV/mm @Thickness 3.00 mm	381 kV/in @Thickness 0.118 in	ASTM D149
Dissipation Factor	0.0010 @Frequency 1000 Hz	0.0010 @Frequency 1000 Hz	ASTM D150
	0.0010 @Frequency 60.0 Hz	0.0010 @Frequency 60.0 Hz	ASTM D150
	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English
Rear Barrel Temperature	366 °C	691 °F
Middle Barrel Temperature	371 °C	700 °F
Front Barrel Temperature	377 °C	711 °F
Nozzle Temperature	382 °C	720 °F
Melt Temperature	366 - 388 °C	691 - 730 °F
Mold Temperature	149 - 177 °C	300 - 351 °F
Drying Temperature	149 °C	300 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Appearance	Beige
	Black
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Fatigue Resistant
	Flame Retardant
	Good Chemical Resistance
	Good Dimensional Stability
	High Heat Resistance
	High Stiffness
	High Strength
Forms	Pellets
Generic	PAEK
Injection Rate	Fast
Processing Method	Injection Molding
	Machining
	Profile Extrusion
Screw Compression Ratio	2.0:1.0 to 3.0:1.0
Uses	Industrial Applications
	Medical Appliances
	Medical/Healthcare Applications