3M Scotch-Weld™ TE040 Polyurethane Reactive Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ TE040 Polyurethane Reactive Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Low viscosity adhesive has a fast set time and is ideal for bonding most wood, plastics, metal and glass.Information provided by 3M
Physical Properties Metric English Comments
Density >= 1.07 g/cc
>= 0.0387 lb/in³
Brookfield Viscosity 7000 cP
7000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 35
35
Tensile Strength at Break 19.0 MPa
2760 psi
ASTM D638 Die C
Elongation at Break 860 %
860 %
ASTM D638 Die C
Tensile Modulus 0.0197 GPa
2.85 ksi
ASMT D638 Die C
Shear Strength 1.79 MPa

@Temperature 82.0 °C
260 psi

@Temperature 180 °F
Overlap, Maple
4.76 MPa

@Temperature 23.0 °C
690 psi

@Temperature 73.4 °F
Overlap, Polystyrene
6.07 MPa

@Temperature 82.0 °C
880 psi

@Temperature 180 °F
Overlap, FRP
6.69 MPa

@Temperature 23.0 °C
970 psi

@Temperature 73.4 °F
Overlap, Maple
7.65 MPa

@Temperature 23.0 °C
1110 psi

@Temperature 73.4 °F
Overlap, Polyacrylic
8.89 MPa

@Temperature 23.0 °C
1290 psi

@Temperature 73.4 °F
Overlap, ABS, Substrate Failure
11.0 MPa

@Temperature 23.0 °C
1590 psi

@Temperature 73.4 °F
Overlap, Polycarbonate
14.5 MPa

@Temperature 23.0 °C
2110 psi

@Temperature 73.4 °F
Overlap, PVC, Substrate Failure
15.9 MPa

@Temperature 23.0 °C
2310 psi

@Temperature 73.4 °F
Overlap, FRP
Peel Strength 3.86 kN/m
22.0 pli
180°, Polystyrene
3.86 kN/m
22.0 pli
T-Peel, Initial, Substrate failure
6.14 kN/m
35.0 pli
T-Peel, Aged 71°C for 2 weeks, Substrate failure
9.12 kN/m
52.0 pli
180°, Aluminum
9.47 kN/m
54.0 pli
180°, Glass
10.5 kN/m
60.0 pli
180°, Polycarbonate
11.4 kN/m
65.0 pli
180°, ABS
11.6 kN/m
66.0 pli
180°, FRP
11.7 kN/m
67.0 pli
180°, Polyacrylic
15.8 kN/m
90.0 pli
180°, PVC, Cotton duck failed during testing
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 0.667 min
0.0111 hour
Set Time