- Sax Polymers SAXALEN PPH329B20 Polypropylene Homopolymer, 20% Glass Filled
Sax Polymers SAXALEN PPH329B20 Polypropylene Homopolymer, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPH329B20 Polypropylene Homopolymer, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPH329B20 is a 20% glass beads filled Polypropylene - Homopolymer intended for injection molding. Low shrinkage, low warpage gradeInformation provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 100 % | 100 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 40.0 MPa | 5800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.100 J/cm² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 100 °C | 212 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- MV Labs B900 BPO4 Boron phosphate
- RedEye On Demand ABSi Translucent ABS with Higher Impact Strength for Rapid Prototyping
- MV Labs SM810 Sm2O3 Samarium oxide
- LyondellBasell Astryn 68F4-2 Polypropylene Homopolymer, 20% Talc
- SPS Guang Zhou POBUXâ„¢ 3001G30 Flame-retarded/GF30%-PBT
- Teijin Multilon DN-1530B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
- Chevron Phillips Marlex® KN 226 LDPE Injection Molding Resin
- Cyclewood Solutions Xylomer™ XM2-FPC Sustainable Injection Molding Resin
- Fainplast Compounds HGK 79 Flexible PVC, Sheathing for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved