Seals Eastern 5514 Polyacrylate Rubber
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 5514 Polyacrylate Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose Natural RubberInformation provided by Seals Eastern, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D297, 15 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 70 | >= 70 | ASTM D2240, Type A |
| 85 | 85 | AVG; ASTM D2240, Type A | |
| Tensile Strength at Break | >= 11.29 MPa | >= 1638 psi | ASTM D412 Method A |
| 11.98 MPa | 1738 psi | AVG; ASTM D412 Method A | |
| Tensile Strength, Yield | 2.15 MPa | 312 psi | AVG Stress at Elongation M25; ASTM D412 Method A |
| >= 2.53 MPa | >= 367 psi | Stress at Elongation M50; ASTM D412 Method A | |
| 4.42 MPa | 641 psi | AVG Stress at Elongation M50; ASTM D412 Method A | |
| 5.30 MPa | 769 psi | AVG Stress at Elongation M100; ASTM D412 Method A | |
| Elongation at Break | >= 280 % | >= 280 % | ASTM D412 Method A |
| 293 % | 293 % | AVG; ASTM D412 Method A | |
| Modulus of Elasticity | 0.01152 GPa | 1.671 ksi | ASTM D412 Method A |
| Shear Modulus | 0.00384 GPa | 0.557 ksi | ASTM D412 Method A |
| Secant Modulus | 0.01083 GPa | 1.571 ksi | ASTM D412 Method A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy / Unit Volume at 20% Elongation (psi) | 30 |
Users viewing this material also viewed the following:
- NextGen Adhesives P907-03 Fiber Optic Adhesive
- Hexion Bakelite™ PF 13 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- Solvay Specialty Polymers Algoflon® D 1610 F Polytetrafluoroethylene (PTFE)
- Stir SpA CT 53 ATC (PVC)
- Total EVA 1005 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film
- Dow Corning SYL-OFF® SL 9112 COATING
- Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, 50% RH
- EMS-Grivory Grivory® XE 4101 black 9225 PA*-GF40
- Ensinger Tecapeek® XP-100 Compression Molded PEEK Compound, Bearing Grade Material with 10% Graphite, 10% PTFE, and 10% Carbon Fiber
- 3M 2A12 (Clear) Co-Extruded Polyethylene Protective Tapes
Copyright © lookpolymers.com All Rights Reserved