EPICHEM Epinyl PA 66 GF25 AU Polyamide 66, 25% Glass, Self extinguishing
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | EPICHEM srl |
| Trade Name | Epinyl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epinyl PA 66 GF25 AU Polyamide 66, 25% Glass, Self extinguishing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: 25% glass fibre filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 1.9 % @Temperature 23.0 °C |
1.9 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0090 cm/cm | 0.0030 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638, ISO R527 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638, ISO R527 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.700 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.31 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 110 °C | 230 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Hot Ball Pressure Test | 220 °C | 428 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 235 °C @Load 5.00 kg |
455 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 250 °C @Load 0.999 kg |
482 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.3 @Frequency 1000 Hz |
3.3 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.015 @Frequency 1000 Hz |
0.015 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 350 V | 350 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Nye Lubricants 634B (SO) Synthetic Oil
- Chevron Phillips KN 230 LDPE Injection Molding Resin (discontinued **)
- Industrial Laminates/Norplex NP629 Paper Base Laminate
- Gromax BFG30-FU00B3 Nylon 6 30% Glass Filled (Conditioned)
- Momentive Performance Materials RTV5812 One-Component, Modified Alkoxy Adhesive Sealant, White
- Chase Plastics CP Pryme® AC100 Acetal Copolymer
- Clariant Renol PA123 Nylon 66, Impact Modified, Heat Stabilized, Lubricated
- Beijing Evergrow Resources TBG Glass Fiber Tissue
- Techmer ES Luriblend® POM HO TL20 BK Acetal
Copyright © lookpolymers.com All Rights Reserved