- Huntsman IROGRAN® A 88 H 4622 TPU-Polyester
Huntsman IROGRAN® A 88 H 4622 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 88 H 4622 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 88 H 4622 is a black colored thermoplastic polyether/polyester-polyurethane for injection molding and extrusion applications. Additional characteristics of the product are high extrudability and low-adhesion surfaces.Performance Features: High hydrolysis resistance Low-adhesion surfaces Good melt flow High production rates High wear resistance Applications: For the production of jackets for high pressure hoses, jacket material for cables hoses, profiles.Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | Injection molded parts |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Injection molded; ASTM D955 |
| Melt Index of Compound | 75 g/10 min @Load 21.6 kg, Temperature 190 °C |
75 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 36 | 36 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 39.0 MPa | 5660 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 650 % | 650 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00700 GPa | 1.02 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.0110 GPa | 1.60 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 65.0 kN/m | 371 pli | Injection molded parts; ASTM D624 |
| Abrasion | 45 | 45 | mm<sup>3</sup>, Injection molded; ISO 4649 |
| Compression Set | 25 % @Temperature 22.8 °C, Time 86400 sec |
25 % @Temperature 73.0 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 122 - 175 °C | 252 - 347 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Middle Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Malvern Minerals Novacite® Daper Untreated Lamellar Quartz Filler/Extender
- Kinetics MIM Ni as Sintered
- Ipiranga Petrochem PH 0320 Polypropylene
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- Formosa Plastics Formolon® 676 PVC
- Teknor Apex Uniprene® UN-2533A Thermoplastic Vulcanizate
- Covestro Desmopan® DP 1350D Polyurethane
- Dow LDPE 132I Low Density Polyethylene, Blown Film Grade
- Austin Novel Materials Texalan® 698A Polyester and Polyether based TPU
Copyright © lookpolymers.com All Rights Reserved