Arkema Group Rilsan® AESN G9 T6L Nylon 12, Graphite Filled (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Graphite Filled
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® AESN G9 T6L Nylon 12, Graphite Filled (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Designation ISO 1874-PA12,EHLS,22-010,CD10Rigid grade with graphite fillers for extrusion. Available color: steel gray. Reinforced light and heat stabilizing agents.Very low friction coefficient. No need of lubricant. Excellent wear and chemical resistance. Long service life.Example applications: Control cables tubing, parking brake control cable, cable for opening doors.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³
Melt Flow	2.1 g/10 min @Load 2.16 kg, Temperature 235 °C	2.1 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	45.0 MPa	6530 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	7.0 %	7.0 %	50 mm/min
Tensile Modulus	2.20 GPa	319 ksi	1 mm/min
Charpy Impact Unnotched	13.3 J/cm²	63.3 ft-lb/in²
	11.1 J/cm² @Temperature -30.0 °C	52.8 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	0.450 J/cm²	2.14 ft-lb/in²
	0.420 J/cm² @Temperature -30.0 °C	2.00 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature 20.0 °C	44.4 µin/in-°F @Temperature 68.0 °F
Melting Point	174 °C	345 °F	(Dry)
Deflection Temperature at 0.46 MPa (66 psi)	162 °C	324 °F
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm