| Category | Polymer , Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMINEX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMINEX® 2140 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO R 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO-DIS 527 |
| Tensile Modulus | 6.00 - 8.00 GPa | 870 - 1160 ksi | DIN 53457 |
| Flexural Strength | 80.0 MPa | 11600 psi | DIN 54352 |
| Compressive Strength | 150 MPa | 21800 psi | ISO 604 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | DIN 53453 |
| Izod Impact Resistance | 2.50 J/cm² | 11.9 ft-lb/in² | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 - 30.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.33 - 16.7 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous |
| 150 °C | 302 °F | Intermittent |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Moisture Absorption at Equilibrium | 450 mg | DIN 53472 |
Users viewing this material also viewed the following:
- MV Labs DY810 Dy2O3 Dysprosium oxide
- Pyrotek Inconel Mesh Core
- Polykemi AB POLYfill PPH K20040 Polypropylene Homopolymer, Mineral Reinforced
- Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced
- Eastman 5267 LDPE 6.5% EVA Copolymer, Clarity, Ultra-high Impact Film Resin (discontinued **)
- Indorama StarPet Preformance® ES11 PET Resin
- Dow Corning 939 EMULSION
- 3D Systems Accura® accuGen™ HC and Ar Plastic for the SLA® 500 System
- Arkema Group OREVAC® 18211 Maleic Anhydride Grafted EVA Copolymer
- Arlon 51576R027 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved