- Schwartz Technical Plastics LAMINEX® 2100 Cotton Fabric, Phenolic Resin Impregnated
Schwartz Technical Plastics LAMINEX® 2100 Cotton Fabric, Phenolic Resin Impregnated
| Category | Polymer , Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMINEX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMINEX® 2100 Cotton Fabric, Phenolic Resin Impregnated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO R 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO-DIS 527 |
| Tensile Modulus | 6.00 - 8.00 GPa | 870 - 1160 ksi | DIN 53457 |
| Flexural Strength | 80.0 MPa | 11600 psi | DIN 54352 |
| Compressive Strength | 150 MPa | 21800 psi | ISO 604 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | DIN 53453 |
| Izod Impact Resistance | 2.50 J/cm² | 11.9 ft-lb/in² | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 - 30.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.33 - 16.7 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous |
| 150 °C | 302 °F | Intermittent |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 5.0 | 5.0 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KC100 | DIN 53480 |
| Moisture Absorption at Equilibrium | 450 mg | DIN 53472 |
Users viewing this material also viewed the following:
- Nye Lubricants 570H-25 (NT) Synthetic Oil
- Orion Engineered Carbons ECORAX® 1720 Carbon Black
- P & P Technology Expanded Neoprene
- SABIC Innovative Plastics Lexan® FST9705 PC Copolymer
- Silikony Polskie Polsil OM 2000 Methyl Silicone Fluid
- Teknor Apex APEX® 583 Polyvinyl Chloride, Flexible
- Williams Advanced Alloys Wambraze™ WB1037 Solder
- ExxonMobil LDPE LD 312.82 Low Density Polyethylene Resin
- Bohler-Uddeholm BÖHLER M268 VMR® Plastic Mold Steel
- Bostik 2128 Clear, Light Assembly EVA Glue Stick
Copyright © lookpolymers.com All Rights Reserved