- Sax Polymers SAXAMID 226F10 Nylon 6.6, 50% Glass Fiber
Sax Polymers SAXAMID 226F10 Nylon 6.6, 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 226F10 Nylon 6.6, 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 226F10 is a polyamide 6.6 injection-molding-grade reinforced with 50% glass fibers. It has high mechanical strength.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 255 MPa | 37000 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 15.5 GPa | 2250 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 290 MPa | 42100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 12.3 GPa | 1780 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m² @Temperature -30.0 °C |
45.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 103 kJ/m² @Temperature 23.0 °C |
49.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 10.7 J/cm² @Temperature 23.0 °C |
50.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 255 °C | 491 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs SN550 (NH4)2SnF6 Ammonium hexafluorostannate(IV)
- Polyplastic TechnoTep B® 45 D Thermoplastic Elastomer, Mineral Filled
- Pyrotek Pyrocast AR-S Castable Refractory
- PolyOne Geon™ Vinyl Wire & Cable WY66L Polyvinyl Chloride, Flexible (PVC, Flexible)
- DSM Akulon® S223-P2 Impact Modified Nylon 66 (European Grade) (Dry) (discontinued **)
- 3M Dyneon™ TF 9201 PTFE (discontinued **)
- Samsung Cheil Industries Infino® SC-1220UR PC, Unreinforced
- A. Schulman PP 1449-01 Polypropylene General-Purpose Homopolymer Polypropylene
- DuPont Teijin Films Mylar® HR951 Polyester Film, 92 Gauge
Copyright © lookpolymers.com All Rights Reserved