- Sax Polymers SAXAMID 126H Nylon 6, Injection Molding Grade
Sax Polymers SAXAMID 126H Nylon 6, Injection Molding Grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126H Nylon 6, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126H is a general purpose polyamide 6 injection-molding-grade. Benefits are short cycle times and good release properties. Additionally it has a higher content of heat stabilizer which is preferred used at higher temperatures.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 9.5 % | 9.5 % | Sim. ISO 62 |
| Moisture Absorption | 3.00 % | 3.00 % | Sim. ISO 62 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 82.0 MPa | 11900 psi | 50 mm/min; ISO 527-1 |
| Elongation at Break | 13 % | 13 % | 50 mm/min; ISO 527-1 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 203 °C | 397 °F | B/120; ISO 306 |
| Glow Wire Test | 750 °C | 1380 °F | GWFI; IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Ritelok GM15 General Purpose Gasket Maker
- Kolon KOPA® KN333HRBL Heat Resistant Nylon 66
- Saint-Gobain CHR® 2283-2 Extruded PTFE Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Solvay IGEPAL® DM 730 Surfactant
- A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene
- Total PSC 523 Polystyrene
- CMW® D355F Pre-oxidized Silver Cadmium Oxide Contact Material ASTM B781 Table 3
- BASF Ultramid® A3L HP BK20465 PA66 (Dry)
- Toyobo E1080A Thermoplastic Polyurethane Elastomer, Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved