SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing milled Glass and PTFE. Added features include; Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.90 GPa | 856 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 1850 x 10-8 mm³/N-M | 920 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 102 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- LG Chemical LUPOY SC2202 PC+GF20%, High Impact
- Sylvin Technologies 9077-75 Natural PVC for Injection Molding
- Stir SpA SG 69 ATC (PVC)
- Silikony Polskie Silpasta R Silicone Paste
- Eagle Brass 19210 XP-10 Copper Iron, Hard
- BASF Ultramid® 8202 PA6 (Dry)
- Ashley Polymers Ashlene® 528LS Nylon 66
- Chang Chun Plastic PBT2100 Fire Retardant PBT
Copyright © lookpolymers.com All Rights Reserved