Samyang Triloy® 450N Polymer Alloy, Blow Molding
| Category | Polymer , Thermoplastic |
| Manufacturer | Samyang |
| Trade Name | Triloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triloy® 450N Polymer Alloy, Blow Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent impact, formability and weather resistance.450N is a blow molding grade.Applications: ConnectorsInformation provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 250 °C |
6.0 g/10 min @Load 8.38 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength | 63.7 MPa | 9250 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | ASTM D790 |
| Izod Impact, Notched | 7.85 J/cm @Thickness 3.17 mm |
14.7 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 83.0 µm/m-°C | 46.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+16 ohm-cm | 3.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 | 3.0 | ASTM D150 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 | 0.0090 | ASTM D150 |
| Arc Resistance | 121 sec | 121 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Humiseal 1A27LSE Urethane Conformal Coating
- Lehmann & Voss LUVOCOM® 1-RG 2 Polyamide 66, with carbon fiber, heat stabilized
- Karina E 32/214-IE MBU Orange Color Concentrate
- Multibase Multibatch® MP 52206 Sheet Extrusion
- SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Europe-Africa-Middle East)
- Saint-Gobain Chemfab® 3 Primary PTFE-Coated Glass
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR MBT
- Eagle Brass 240 Low Brass, Extra Spring
- Clariant Renol PCSP0015 Polycarbonate, Carbon Fiber Filled
- 3M Safety-Walk™ 770 Gray Coarse Tapes and Treads
Copyright © lookpolymers.com All Rights Reserved