Samyang Triloy® 410N PC/PET alloy, Flame Retardant (discontinued **)

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Samyang Triloy® 410N PC/PET alloy, Flame Retardant (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Impact resistantHeat resistantDimensional stabilityProcessabilityFlame retardantApplications:O/A partRear view mirror housingRice cooker baseAll information provided by Samyang

Physical Properties	Metric	English	Comments
Specific Gravity	1.25 g/cc	1.25 g/cc	ASTM D792
Water Absorption	0.15 % @Time 86400 sec	0.15 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage	0.0070 - 0.012 cm/cm @Thickness 3.00 mm	0.0070 - 0.012 in/in @Thickness 0.118 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115	ASTM D785
Tensile Strength, Yield	53.9 MPa	7820 psi	ASTM D638
Elongation at Break	80 %	80 %	ASTM D638
Flexural Yield Strength	81.4 MPa	11800 psi	ASTM D790
Flexural Modulus	2.26 GPa	327 ksi	ASTM D790
Izod Impact, Unnotched	5.88 J/cm @Thickness 3.17 mm	11.0 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	83.0 µm/m-°C	46.1 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	105 °C	221 °F	ASTM D648
Flammability, UL94	V-0 @Thickness 1.59 mm	V-0 @Thickness 0.0625 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.00e+16 ohm-cm	3.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.0 @Frequency 1.00e+6 Hz	3.0 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	23.0 kV/mm	584 kV/in	ASTM D149
Dissipation Factor	0.0090 @Frequency 1.00e+6 Hz	0.0090 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	121 sec	121 sec	ASTM D495

Processing Properties	Metric	English
Rear Barrel Temperature	230 - 250 °C	446 - 482 °F
Middle Barrel Temperature	220 - 240 °C	428 - 464 °F
Front Barrel Temperature	210 - 230 °C	410 - 446 °F
Nozzle Temperature	240 - 250 °C	464 - 482 °F
Melt Temperature	240 - 250 °C	464 - 482 °F
Drying Temperature	120 °C	248 °F
Dry Time	3 - 5 hour	3 - 5 hour
Moisture Content	<= 0.020 %	<= 0.020 %
Screw Speed	30 - 80 rpm	30 - 80 rpm