Dow AFFINITY™ PL 1881G Polyolefin Plastomer (POP)

Category Polymer , Film , Thermoplastic , Polyolefin
Manufacturer Dow Chemical
Trade Name AFFINITY™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow AFFINITY™ PL 1881G Polyolefin Plastomer (POP).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AFFINITY™ PL 1881G Polyolefin Plastomer (POP) is produced via INSITE™ Technologies. It is designed for use in a variety of packaging applications, including high-speed, form-fill-seal products.Information provided by Dow
Physical Properties Metric English Comments
Density 0.9035 g/cc
0.03264 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Antiblock Level 2500 ppm
2500 ppm
Slip Level 750 ppm
750 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.07 MPa
1170 psi
ASTM D882
Film Tensile Strength at Yield, TD 7.17 MPa
1040 psi
ASTM D882
Film Elongation at Break, MD 585 %
585 %
ASTM D882
Film Elongation at Break, TD 630 %
630 %
ASTM D882
Secant Modulus, MD 0.0970 GPa
14.1 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.0970 GPa
14.1 ksi
2% Secant; ASTM D882
Impact 18.5
18.5
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
265
265
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Puncture Energy 8.09 J
5.97 ft-lb
Dow Method
Coefficient of Friction, Dynamic 0.15
0.15
film/film; ASTM D1894
Elmendorf Tear Strength MD 560 g
560 g
Modified rectangular test specimen; ASTM D1922
Elmendorf Tear Strength TD 730 g
730 g
Modified rectangular test specimen; ASTM D1922
Elmendorf Tear Strength, MD 11.0 g/micron
280 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 14.4 g/micron
365 g/mil
ASTM D1922
Dart Drop Test >= 830 g
>= 1.83 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 45.4 MPa
6580 psi
ASTM D882
Film Tensile Strength at Break, TD 42.5 MPa
6170 psi
ASTM D882
Heat Seal Strength Initiation Temperature 85.0 °C
185 °F
2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 100 °C
212 °F
Dow Method (DSC)
Vicat Softening Point 86.0 °C
187 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 3.2 %
3.2 %
ASTM D1003
Gloss 112 %
112 %
20°; ASTM D2457
Transmission, Visible 83 %
83 %
Clarity; ASTM D1746
Descriptive Properties Value Comments
Block Force g 70
ASTM D3354-89