Samsung Cheil Industries Starex® VE-0856 (VE-0856U UV) Flame Retardant Grade ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® VE-0856 (VE-0856U UV) Flame Retardant Grade ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VE-0856U is the UV-Stabilized Version.Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
Water Absorption 0.30 %
0.30 %
ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
ASTM D955
Melt Flow 33 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 33 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell R 97
97
ASTM D785
Tensile Strength, Yield 39.3 MPa

@Thickness 3.17 mm
 5700 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 15 %

@Thickness 3.17 mm
 15 %

@Thickness 0.125 in
 ASTM D638
Flexural Strength 55.2 MPa

@Thickness 3.17 mm
 8000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.28 GPa

@Thickness 3.17 mm
 330 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 1.76 J/cm

@Thickness 6.35 mm
 3.30 ft-lb/in

@Thickness 0.250 in
 ASTM D256
2.46 J/cm

@Thickness 3.17 mm
 4.60 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 78.9 °C

@Thickness 6.35 mm
 174 °F

@Thickness 0.250 in
 Unannealed; ASTM D648
Vicat Softening Point 90.0 °C
194 °F
Unannealed; ISO R 306
Flammability, UL94 5VB
5VB
UL94
5VA
5VA
UL94
V-0

@Thickness 2.50 mm
 V-0

@Thickness 0.0984 in
 UL94
V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
 UL94
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 180 °C
338 - 356 °F
Middle Barrel Temperature 190 - 200 °C
374 - 392 °F
Front Barrel Temperature 200 - 210 °C
392 - 410 °F
Melt Temperature 210 - 220 °C
410 - 428 °F
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 58.80 - 108 MPa
8528 - 15600 psi
Back Pressure 0.689 - 1.38 MPa
100 - 200 psi
Screw Speed 50 - 70 rpm
50 - 70 rpm
Descriptive Properties Value Comments
UV Resistance <3 Delta E
300 Hr. Ivory Color; ASTM D4459