- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® SR-0305 ABS, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® SR-0305 ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SR-0305 ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Temperature 23.0 °C |
0.050 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 17 g/10 min @Load 10.0 kg, Temperature 220 °C |
17 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 45.1 MPa | 6540 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.26 J/cm @Thickness 6.35 mm |
4.22 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.35 J/cm @Thickness 3.17 mm |
4.41 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL4019 PC (Asia Pacific)
- Indium Corp. Indalloy 17 Low Melting Bismuth Alloy
- Menzolit Menzolit® BMC 0170 Unsaturated Polyester UP
- Lubrizol Advanced Materials PEARLTHANE® 11T95P Thermoplastic Polyurethane Elastomer
- Hardwire 3x2 Cord
- Karina E 811-40/312-IS-RG Green PVC Compound
- Fiberfil® J-60/15/MI/20 Polypropylene Homopolymer, 35% Glass/mica Reinforced
- Samsung Cheil Industries Starex® BC-0130 X ABS, Unreinforced General Purpose
- Tra-Con Tra-Duct 921U02 Long Pot Life Silver-Filled Epoxy
- Dow INSPIRE™ D118.01 Developmental Performance Polymer
Copyright © lookpolymers.com All Rights Reserved