- Nilit FRIANYL A63 TF-KV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass ball reinforced
Nilit FRIANYL A63 TF-KV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber/PTFE Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 TF-KV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 - 1.3 % | 0.30 - 1.3 % | ISO 62 |
| Water Absorption at Saturation | 3.5 - 5.5 % | 3.5 - 5.5 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 163 MPa | 23600 psi | ISO 2039-1 |
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527 |
| Tensile Modulus | 4.10 GPa | 595 ksi | ISO 527 |
| Flexural Strength | 89.0 MPa | 12900 psi | ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 2.70 J/cm² @Temperature -40.0 °C |
12.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | DIN 53453 |
| 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA | |
| 0.300 J/cm² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 140 °C | 284 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Quantum Composites QC-2150LD NT 25% Fiberglass Reinforced Phenolic SMC
- Polymer Resources NY6/12-G43 Nylon 612, 43% Glass Reinforced
- ExxonMobil Escorene® LL-3105 LLDPE/Hexene Premium Film Resin, Tough (discontinued **)
- SABIC Innovative Plastics Valox® HX215HP PBT
- Sawbones Solid Rigid Polyurethane Foam 5 pcf Density
- Shin-Etsu Silicones KSG-326 Fluid
- Addiplast Addinyl B2 G10 V20 Nylon 6, Glass/Mineral Filled
- Aptek 6512-PMF Electronic grade, conductive epoxy adhesive
- Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled
Copyright © lookpolymers.com All Rights Reserved