- Samsung Cheil Industries Starex® SF-0941 MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Starex® SF-0941 MABS, Unreinforced Scratch Resistant
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SF-0941 MABS, Unreinforced Scratch Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 26 g/10 min @Load 10.0 kg, Temperature 250 °C |
26 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 48.1 MPa | 6980 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 23 % | 23 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 81.4 MPa | 11800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.755 J/cm @Thickness 6.35 mm |
1.41 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.755 J/cm @Thickness 3.17 mm |
1.41 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | B/50; ISO R306 |
| 105 °C | 221 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREWHITE PP 51-50
- PolyOne Geon™ 140 Series 140X466 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Mearthane Durethaneâ„¢ S DS-695A Solid Polyurethane Elastomer
- A. Schulman POLYBATCH™ MAS-25 Concentrate Based In LDPE
- Ter Hell Plastic Terez® PC X 9005 GF 5 Polycarbonate, 5% Glass Fiber
- ChevronTexaco Dura-Lith® NLGI 000 Grease EP
- ExxonMobil HDP8760.29 Rotational Molding Resin
- Arlon 90B32R016AC Aluminum Clad Press Pad with "C-Finish"
- Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound (discontinued **)
- Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C)
Copyright © lookpolymers.com All Rights Reserved