SCG Chemicals EL-Proâ„¢ P401S Polypropylene Flat Yarn/Sheet
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Fiber Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P401S Polypropylene Flat Yarn/Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics: Excellent mechanical propertiesRecommended Applications:Stretch tape for jumbo woven sheetMonofilament for rope and sheetInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 500 hour @Temperature 50.0 °C |
>= 500 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1693 |
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Flexural Modulus | 1.397 GPa | 202.7 ksi | ASTM D790 |
| Izod Impact, Notched | 0.177 J/cm @Temperature -20.0 °C |
0.331 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 0.275 J/cm @Temperature 0.000 °C |
0.514 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.412 J/cm @Temperature 23.0 °C |
0.771 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Vicat Softening Point | 155 °C | 311 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 50 % @Thickness 1.00 mm |
50 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 85 % @Thickness 1.00 mm |
85 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering C70G Chloroprene Rubber
- Noble Polymers Regis™ 225104 Thermoplastic Olefin (TPO)
- Solvay Chemicals 2,2,2-Trifluoroethanol
- Plenco 6401 Phenolic, Briquette, Transfer Molded
- Weartech International WT-306 Cobalt Hardfacing & Wear Resistant Alloy
- Toyobo Diaflora® FD 2220B
- Dow Corning SYL-OFF® 7950 EMULSION COATING
- A. Schulman ComAlloy Hiloy® 263 Glass Reinforced, Modified SMA
Copyright © lookpolymers.com All Rights Reserved