- Styrolution Novodur® H801 ABS / PC
Styrolution Novodur® H801 ABS / PC
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® H801 ABS / PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur H801 is a high heat injection molding grade with high impact strength and reduced emission.Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527 |
| Charpy Impact Unnotched | 16.0 J/cm² @Temperature -30.0 °C |
76.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 22.0 J/cm² @Temperature 23.0 °C |
105 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75 |
| Vicat Softening Point | 105 °C @Load 5.10 kg |
221 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 38.0 kV/mm @Thickness 1.50 mm |
965 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 °C | 464 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- NextGen Adhesives P907-03 Fiber Optic Adhesive
- Radici Radiflam® BN100 AE Polybutylene Terephthalate
- SABIC Innovative Plastics NORYL V01550 PPE+HIPS (Europe-Africa-Middle East)
- UBE UBEPOL B -B HIPS (Low-cis)
- Epoxy Technology EPO-TEK® H20E-LV Electrically Conductive, Silver Epoxy
- DuPont Teijin Films Mylar® MLB Polyester Film, 48 Gauge
- BASF Ultramid® C31 01 PA6/66
- 3M 7220SA Screen Printable Polyester Performance Label Products with Structured Adhesive
- DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**)
- ExxonMobil Febis K Series 68
Copyright © lookpolymers.com All Rights Reserved