Samsung Cheil Industries Infino® GW-1030S PC, Unreinforced Recycled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GW-1030S PC, Unreinforced Recycled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 250 °C |
18 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 67.7 MPa | 9820 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 107 % | 107 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.01 GPa | 292 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.88 J/cm @Thickness 6.35 mm |
11.0 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 7.85 J/cm @Thickness 3.17 mm |
14.7 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C @Thickness 6.40 mm |
255 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 140 °C | 284 °F | B/50; ISO R306 |
| 144 °C | 291 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
Users viewing this material also viewed the following:
- Radici Radilon® CS 38FL (cond.) Nylon 6/66
- Polymer Resources PPX-GP2 Modified-PPO, General Purpose
- Ravago Manufacturing Americas Hylon® N1000STHLUV2 HF Nylon 6/6 (discontinued **)
- Shin-Etsu Silicones KE-347T Silicone, RTV Coating
- Unifrax FyreWrap® XFP® Expanding Paper
- A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
- BASF Ultramid® 1310-11 NF2001 PA66 (Conditioned)
- BASF Lupranate® MP102 Isocyanate Modified MDI
Copyright © lookpolymers.com All Rights Reserved