Samsung Cheil Industries Infino® GC-1015 PC/ABS, FR
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GC-1015 PC/ABS, FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 63.7 MPa | 9240 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.8 MPa | 8820 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 102 % | 102 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.57 J/cm @Thickness 6.35 mm |
2.94 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 6.96 J/cm @Thickness 3.17 mm |
13.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 6.40 mm |
176 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | B/50; ISO R306 |
| 101 °C | 214 °F | B/120; ISO R306 | |
| UL RTI, Electrical | 95.0 °C | 203 °F | |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | |
| UL RTI, Mechanical without Impact | 90.0 °C | 194 °F | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VB @Thickness 3.00 mm |
5VB @Thickness 0.118 in |
||
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-7905 PEEK, with carbon fiber
- Michelman® Michem® Emulsion 21030 Anionic polyethylene emulsion
- Spartech Weather-Pro G Weatherable Sheet
- Star Plastics PC7523R Molding Grade PC
- Polyram Polytron P50B07 Polypropylene, 50% Long Glass Fiber, UV Stabilized
- ExxonMobil LD331.99 EVA LD 331.99 Very Clear, High Impact Film Resin
- DuPont Teijin Films Mylar® EL Polyester Film, 75 Gauge
- Adell BD-30 Nylon 6, Ultra High Impact
- BASF Pluracol® 9346 Rigid Polyol
- Aremco Pyro-Tape™ 682-PM High Temperature Tape Tri-layer silicone rubber/aluminum foil/ fiberglass with silicone adhesive
Copyright © lookpolymers.com All Rights Reserved