- Diamond Polymers ASA TW-15H
Diamond Polymers ASA TW-15H
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA TW-15H.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, High Heat Resistance, High IzodInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 2.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength, Yield | 42.7 MPa | 6200 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.21 GPa | 320 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.82 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
3.40 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 100 °C | 212 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 120 °C | 248 °F | 0.125 inch, 1 Kg; ASTM D1525 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FF 33 Low Density Polyethylene - Blown Film Extrusion
- NIZHNEKAMSKNEFTEKHIM PE 4052U (52411) High Density Polyethylene
- Mateck Zirconium Oxide Substrate, ZrO2:Y(9.5% Y)
- Momentive Performance Materials AC6069 Boron Nitride (BN) Powder
- A. Schulman POLYBATCH™ Teal 30316 Concentrate Based In LLDPE
- Covestro Apec® HT KU 1-9353 High-Heat Polycarbonate, UV-Stabilized
- ExxonMobil LDPE LD 158JD Low Density Polyethylene Resin
- EPICHEM Epilac ABS-BLACK Acrylonitrile Butadiene Styrene
- Arlon 30400N060 0.060" (1.52 mm) Uncured Silicone Rubber
- BASF Octamethylenediamine
Copyright © lookpolymers.com All Rights Reserved