Samsung Cheil Industries Infino® CF-1030 PC, Unreinforced High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® CF-1030 PC, Unreinforced High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 24 g/10 min @Load 10.0 kg, Temperature 250 °C |
24 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 60.8 MPa | 8820 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.8 MPa | 8820 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 82 % | 82 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 82.4 MPa | 12000 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.55 J/cm @Thickness 6.35 mm |
4.78 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 7.16 J/cm @Thickness 3.17 mm |
13.4 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C @Thickness 6.40 mm |
280 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 143 °C | 289 °F | B/50; ISO R306 |
| 145 °C | 293 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Osprey Metals 80/20 Ni Cr Powder (Grade 90% - 22)
- North Wood Plastics 60 PP + UNIFILL (20% Wood Fiber)
- DuPont Performance Polymers Hytrel® HTR8685 BK022A TPC-ET (Unverified Data**)
- Arlon 0.015" (0.381 mm) Semi-Cured Silicone Traction Motor Insulation with Fiberglass Substrate (51224R015) &n
- Michelman® Michem® Lube 160PF Anionic carnauba wax emulsion
- LyondellBasell Astryn BC78A Polypropylene Copolymer, 23% Talc
- Schwartz Technical Plastics LAMIGAMID® 400 Cast Polyamide 6, Elastomer Modified, Dry
- Sibur KF-Z Carbamide Formaldehyde Resin
- Suzhou Hipro Polymers Hiprolon® 200 NN Nylon 1010, dry
- Bond Laminates TEPEX® dynalite 108-FG290(x)/45% Filament Glass – TPU Consolidated Composite Laminate
Copyright © lookpolymers.com All Rights Reserved