Samsung Cheil Industries Starex® VE-0558 ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VE-0558 ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame-retardant ABS with excellent weather resistance that is used in the exterior of OA devices such as monitors, printers, fax machines, duplicators etc.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength at Break | 26.5 MPa | 3840 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 35.3 MPa | 5120 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.77 GPa | 256 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 53.0 MPa | 7690 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.77 GPa | 256 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.35 mm |
3.67 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.55 J/cm @Thickness 3.17 mm |
4.78 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 6.40 mm |
176 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | B/50; ISO R306 |
| 93.0 °C | 199 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 2.10 - 3.00 mm |
V-0 @Thickness 0.0827 - 0.118 in |
|
| 5VB @Thickness 2.50 - 3.00 mm |
5VB @Thickness 0.0984 - 0.118 in |
Users viewing this material also viewed the following:
- Perstorp Compounds 371 Urea-Formaldehyde w/ cellulose filler
- Ineos Nova FX530 Impact Polystyrene
- Solvay TECHNYL® A 218 PA66, 33% glass fiber, Conditioned
- SABIC Innovative Plastics NORYL LEN2211 PPE+HIPS (Asia Pacific)
- SABIC Innovative Plastics Valox® 451E PBT (Asia Pacific)
- Wellman Wellamid® MR340 42H-N 34% Mineral Reinforced Nylon 6, Heat Stabilized
- Covestro Baydur® STR/C-410 IMR Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System
- ExxonMobil LDPE LD 655 Low Density Polyethylene Resin (European Grade)
- Braskem GM9450F HDPE Blown Film Extrusion Polyethylene
- AorTech Biomaterials Elast-Eon™ E2A Biomedical Polyurethane Pellets
Copyright © lookpolymers.com All Rights Reserved