SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xylex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, US Food Contact compliant, chemically resistant.
This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HX8300HP.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D 1238 |
| 15 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 g/10 min @Load 4.76 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 | 73 | 10S reading; ASTM D 2240 |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D 638 |
| 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D 638 |
| >= 200 % | >= 200 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.52 GPa | 220 ksi | 50 mm/min; ASTM D 638 |
| 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 71.0 MPa | 10300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 1.68 GPa | 244 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 11.2 J/cm @Temperature 23.0 °C |
21.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Impact Test | 95.0 J @Temperature 23.0 °C |
70.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 85.0 °C | <= 185 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C @Thickness 3.20 mm |
174 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 75.0 °C @Thickness 3.20 mm |
167 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 96.0 °C | 205 °F | Rate B/50; ASTM D 1525 |
| 96.0 °C | 205 °F | Rate B/120; ISO 306 | |
| Glow Wire Test | 750 °C @Thickness 1.00 mm |
1380 °F @Thickness 0.0394 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.539 | 1.539 | ISO 489 |
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D 257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D 257 |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC code 0; UL 746A |
Users viewing this material also viewed the following:
- Gwent Electronic Materials C2011009D1 Curable Silver Range
- Techmer ES HiFill® PA6 GF30 HF L BK 30% Glass Filled
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work
- Teknor Apex TEKRON® 4200-70 Thermoplastic Elastomer
- Wall Colmonoy COLMONOY® 228 Custom Formulated Nickel-Based Alloy For Glass
- Trimay® Wear Plate T156 Iron-based Steel Overlay
- API Megol AM T A SEBS Adhesion Modified Overmolding for Polar Polymers
- SABIC Innovative Plastics Lexan® 943 PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved